HDPE 100B
- properties
| Typical properties | Test method | Unit | Value |
| MFI @190°C ,5.0Kg | ASTM 1238 | gr /10min | 0.22 |
| MFI @190°C ,21.6Kg | ASTM 1238 | gr /10min | 6.2 |
| FRR (21.6/5.0) | 28 | ||
| Mass Density (23°C ) | ISO 1183-1 | gr /cm3 | 0.957 |
| Bulk Density | ASTM D D1829 | gr /cm3 | 0.605 |
| Carbon Black Content | ASTM D 4218 | % | 2.3 |
| Carbon Black Dispersion | BS -2782 | Rating | max 3 |
| Impact Strength (charpy Index @23cº) | ISO 179/1eA | mj /mm² | >20 |
| Hydrostatic Strength (80°C /5.5MPa) | ISO 11677 | hr | >165 |
| Volatiles | Basel Method | ppm | 349 |
| Contamination | Hoechst Method | Rating | 2 |
| Vicat Softening Temperature ,(B50 ) | ASTM D D1525 | °C | 75 |
| Oxidation Induction Time ,(210°C ) | ASTM D 3895 | min | >25 |
| DSC Melting Point | °C | 130 | |
| Shore Hardness ,(Shore D ,3sec ) | ASTM D 2240 | 63 |