1102XK
- Properties
| Property | Test Method | Unit | Value |
| MFR (230°C /2.16Kg ) | ASTM D1238 /L | gr /10min | 4 |
| Tensile Modulus of Elasticity (1mm/min ) | ASTM D638 | MPa | 1500 |
| Tensile Strength at Yield (50mm /min ) | ASTM D638 | MPa | 34 |
| Elongation at Yield (50mm /min ) | ASTM D638 | % | 9 |
| Notched Charpy Impact at 23° | ISO 179/1eA | KJ /m2 | 4 |
| Notched Charpy Impact at -30° | ISO 179/1eA | KJ /m2 | 1.7 |
| Vicat Softening Point ,10N | ASTM D1525 | °C | 154 |
| Ball indentation hardness | ISO 2039-1 | MPa | 74 |
| HDT (0.46N /mm2 ) | ASTM D648 | °C | 85 |
| Melting Point ,DSC | ASTM D3417 | °C | 163 |
| Density | ASTM D792 | gr /cm3 | 0.91 |